摘要
Inthisstudy，theweldingthermalcyclecurveexhibitedtwotemperaturepeaksinhighheat-inputtwin-wireseparate-poolsubmerged-arcweldingandcoarse-grainedheataffectedzoneexistedintheweldedjoint.Theinclusionsofprimaryweldmetalandcoarse-grainedheataffectedzoneofCe-addedSAWshouldbeAl203,MnO,Si02,TiO,Ce2S3,CeS,Ce202SandCe203.Undertheeffectofweldingthermalcycle,oxy-sulfidesinclusionsofCe,thediameterofwhichwaslessthan2.0|Jim,slightlygrewlarger,butthecompositionandtypeoftheinclusionsdidn，tchange.ThemicrostructureofthelargeheatinputweldmetalhadacicularferritethatCeoxidesulphideparticlesinducednucleationandproeutectoidferrite.Inthecoarse-grainedheataffectedzoneofweldmetal,home-positionprecipitationofacicularferriteandsympatheticacicularferritewerebothobserved.Itwassupposedthatpreviouscrystalcellsofacicularferriteinaustenitegrainpromotedhome-positionprecipitationofacicularferrite.Meanwhile,sympatheticacicularferritetendedtonucleateattheprimaryacicularferritegrainboundaries,wherehighdislocationdensitywaslocated,andgrewinsidetheneighboringcarbon-depletedausteniticregions.Thegranularbainitenucleatedintheausteniticzonewithhighcarboncontentclosetoacicularferriteandsympatheticacicularferrite.
出版日期
2017年01月11日（中国Betway体育网页登陆平台首次上网日期，不代表论文的发表时间）