摘要
AseriesofLa2O3/MCnylonnanocompositeswerepreparedviainsitupolymerization.Theeffectsofcontentofnano-La2O3onthemechanicalpropertiesofnanocompositeswerestudied.Dispersionofnano-La2O3inMCnylonmatrixwasobservedwithSEM.ThecrystalstructureofnanocompositeswascharacterizedbymeansofXRD.SEManalysisshowsthatLa2O3nanoparticlesareuniformlydispersedinMCnylonmatrixandlittleclusteringexistswhenthecontentofnano-La2O3islowerthan1%,however,whenthecontentofnano-La2O3ismorethan1%,itbeginstocluster.XRDanalysisindicatsthatnano-La2O3doesnotchangethecrystalstructureofMCnylon.Mechanicalpropertiestestsshowthatthetensilestrength,elongationatbreak,impactstrength,flexuralstrength,andflexuralmodulusofnanocompositesfirstincreasethendecreaseasthecontentofnano-La2O3isincreased.Whenthecontentofnano-La2O3is0.5%,thetensilestrengthandelongationatbreakofnanocompositesreachmaximum,whichare17.9%and52.1%higherrespectivelythanthoseofMCnylon.Whenthecontentofnano-La2O3is1.0%,theimpactstrength,flexuralstrengthandflexuralmodulusofnanocompositesreachmaximum,whichare36.6%,12.7%and16.3%higherrespectivelythanthoseofMCnylon.
出版日期
2005年06月16日（中国Betway体育网页登陆平台首次上网日期，不代表论文的发表时间）