Thepurposeofthisresearchistoquantifytheeffectsofcompositionalandprocessingparametersonthemicrostructureandpropertiesofdualphasesteelproduceddirectlybyhotrollingandrapidcooling.Steelswiththebasecompositionof0.1%C,1.4%Si,and1.0%Mnwithadditionsof0.5%Crtoinfluencehardenability,0.04%Nbtoretardrecrystallizationinthelatterstagesofrolling,or0.02%Titoinhibitgraingrowthduringandafterreheatingwereinvestigated.Investigationwasmadetopredictmicrostructureevolutionandtocorrelatemicrostructurewithprocessingparameters.Theeffectsoftheimportantmicrostructureparameterssuchasferritegrainsize,martensitevolumefraction(VM)andmorphology(polygonalorfibrous)onthetensileandimpactpropertiesarediscussed.Multiplelinearregressionanalysisoftheultimatetensilestrengthhasshownthat,increasingVMandmartensitemicrohardnessandgrainrefinementofferritearethemajorcontributionstoincreasethestrengthofthesteel.Itwasfoundthatthedual-phasesteelproducedbycontrolledrollingprocess,withamicrostructurewhichconsistedoffinegrainedferrite(4μm)and35%～40%fibrousmartensite,presentedoptimumtensileandimpactpropertiesbecauseofenhancedresistancetocrackpropagation.
出版日期
2002年05月15日（中国Betway体育网页登陆平台首次上网日期，不代表论文的发表时间）